6082 T651 Aluminum Plate Sheet
Certification: ASTM/EN 485 Complete Specifications
We strictly control the quality of the 6082 T651 Aluminum Plate Sheet, ensuring that each sheet meets the highest industry standards, stable performance, and competitive price.
Table of Contents- 7 Key Reasons for Choosing 6082 T651 Aluminum Plate
- 6082 T651 Aluminum Plate Common Specifications
- Aluminum 6082 t651 Applications
- 6082 T651 Aluminum vs 6082 T6 Aluminum Plate
6082-T651 aluminum plate/sheet refers to an aluminum alloy plate/sheet that has undergone solution heat treatment, quenching, and artificial aging to reach the T651 state. Here is some information about 6082-T651 Aluminum Sheet/Sheet:
- Strength and Mechanical Properties: 6082-T651 Aluminum has high strength and excellent mechanical properties.
- It has a tensile strength ranging from 310 to 340 MPa (45, 000 to 49, 000 psi)
- Yield strength is approximately 260 MPa (38, 000 psi).
6082 T651 Aluminum Alloy exhibits good formability, weldability, and corrosion resistance.
- Machinability: While 6082-T651 has good machinability, due to its higher strength than other aluminum alloys, it is important to use proper cutting tools and machining techniques.
- Certification: 6082-T651 Aluminum Plate/Sheet can meet industry standards and certifications such as ASTM B209 (American Society for Testing and Materials) and EN 485 (European Standard).
7 Key Reasons for Choosing 6082 T651 Aluminum Plate
Seven key reasons to choose 6082 T651 aluminum plate over other Temper’s 6082 aluminum alloys, along with specific application examples for each reason:
Reason 1: 6082 T651 aluminum plate has a high tensile strength
High Strength: 6082 T651 aluminum plate has high tensile strength, making it suitable for applications where structural integrity and strength are critical. It has a good balance of strength and weight, which is very important in industries such as aerospace and automotive.
Application examples: Structural components in aerospace, such as aircraft fuselages and wings, where the strength-to-weight ratio is critical.
Reason 2: The 6082 T651 aluminum plate is easy to machine.
Workability: It is easy to work with, meaning it can be easily cut, shaped, and machined into a variety of components. This makes it the first choice for industries requiring complex parts.
Application examples: Precision parts in the automotive industry, such as engine components and suspension components, require complex machining.
Reason 3: 6082 T651 aluminum is naturally corrosion-resistant
Corrosion Resistance: Generally speaking, aluminum is naturally resistant to corrosion due to its oxide layer. 6082 T651 aluminum plate is no exception, making it suitable for outdoor and marine applications.
Application examples: Marine applications, including hulls and components that are frequently exposed to salt water.
Reason 4: 6082 T651 aluminum is easy to weld
Weldability: Welding can be done using a variety of methods, which is critical for industries that need to join aluminum components.
Application examples: Fabrication of aluminum structures in buildings, such as bridges and frames.
Reason 5: T651 condition provides stable mechanical properties
Heat treatable: T651 status indicates that the aluminum alloy has undergone a heat treatment process. This state provides excellent mechanical properties and stability, making it suitable for applications requiring consistent performance at different temperatures.
Application examples: Aerospace components such as landing gear and structural components must maintain consistent performance at different temperatures.
Reason 6: Aluminum alloys such as 6082 are suitable for anodized
Anodizability: Aluminum alloys such as 6082 can be easily anodized to improve their corrosion resistance, wear resistance, and add decorative properties.
Application examples: Construction applications, such as decorative panels and facades, where corrosion resistance and aesthetics are important.
Reason 7: 6082 T651 Aluminum offers a good balance between cost and performance
Cost-Effectiveness: While aluminum alloys may be more expensive than some other materials, they offer a good balance between cost and performance, especially when considering their durability and low maintenance requirements.
Application examples: Consumer electronics where a lightweight and durable housing or chassis is required at a reasonable cost.
How the specific properties of 6082 T651 aluminum make it suitable for a variety of industries and applications, each benefiting from one or more of its key attributes. Choosing the appropriate tempering temperature ensures that the material meets the specific performance and durability requirements of a given application, making it a versatile choice within the aluminum alloy family.
6082 T651 Aluminum Plate Common Specifications
| Specification | Common Options/Range |
|---|---|
| Thickness | 0.5mm-300mm |
| Width | 500-2650mm |
| Length | 500-12000mm |
| Surface Finish | Mill finish, polished, color coated , anodized |
| Standards/Certifications | ASTM, EN, A96082, BS L113, BSL115, BS HP30, BS HS30, ETC |
Common Thicknesses of 6082 T651 Aluminum Plate
| Product | Common Thickness (mm) | Common Thickness (inches) |
|---|---|---|
| 6082 T651 Aluminum Plate | 6 | 0.236 |
| 6082 T651 Aluminum Plate | 8 | 0.315 |
| 6082 T651 Aluminum Plate | 10 | 0.394 |
| 6082 T651 Aluminum Plate | 12 | 0.472 |
| 6082 T651 Aluminum Plate | 15 | 0.591 |
| 6082 T651 Aluminum Plate | 20 | 0.787 |
| 6082 T651 Aluminum Plate | 25 | 0.984 |
| 6082 T651 Aluminum Plate | 30 | 1.181 |
| 6082 T651 Aluminum Plate | 35 | 1.378 |
| 6082 T651 Aluminum Plate | 40 | 1.575 |
| 6082 T651 Aluminum Plate | 50 | 1.969 |
| 6082 T651 Aluminum Plate | 60 | 2.362 |
| 6082 T651 Aluminum Plate | 70 | 2.756 |
| 6082 T651 Aluminum Plate | 80 | 3.15 |
| 6082 T651 Aluminum Plate | 100 | 3.937 |
| 6082 T651 Aluminum Plate | 120 | 4.724 |
| 6082 T651 Aluminum Plate | 150 | 5.906 |
Aluminum 6082 t651 Applications
Typical Uses: Due to its combination of strength, formability, and corrosion resistance, 6082-T651 Aluminum Sheet/Sheet is used in a variety of industries including:
6082 t651 Aerospace Aluminum Plate
Aluminum 6082 T651 is used in structural components of aircraft such as wing skins, fuselage panels, and structural supports.
- 6082-T651 Aluminum Alloy: Typically used for structural components.
- Matching alloys and tempers: Matching alloys for aerospace applications can vary according to specific requirements. Common alloys used in aerospace include 7075-T6 and 2024-T351, which are also used in structural components such as wing skins and fuselage panels.
6082 t651 Automotive Aluminum Plate
6082-T651 is used in the manufacture of automotive components such as chassis components, body panels, and structural elements.
- 6082-T651 aluminum alloy: used in various automotive components.
- Matching alloys and tempers: Matching alloys for automotive applications can vary depending on the specific component. Alloys such as 6061-T6 and 5052-H32 are commonly used in automotive parts such as chassis components, body panels, and structural elements.
6082 t651 Marine Aluminum Plate
6082-T651 is suitable for marine applications including shipbuilding, marine components, and offshore structures due to its resistance to saltwater corrosion.
- 6082-T651 aluminum alloy: for hulls, superstructures, and marine fittings.
- Matching Alloys and Conditions: Matching alloys for marine applications may vary. Alloys such as 5083-H321 and 5086-H116 are commonly used in marine structures and hulls due to their excellent corrosion resistance in seawater environments.
Construction
6082-T651 may be used for structural elements, building panels, and facade cladding for architectural projects.
- 6082-T651 aluminum alloy: for structural elements, building panels, and facade cladding.
- Matching alloys and tempers: Alloys such as 6063-T6 and 5052-H32 are commonly used in architectural applications for extruded profiles, sheet metal, and decorative elements.
Industrial Machinery
6082-T651 Aluminum Plate/Sheet is used in a variety of industrial applications such as tooling, mold making, and general manufacturing.
- 6082-T651 aluminum alloy: used in various machinery and equipment components.
- Matching Alloys and Conditions: Matching alloys for machinery and equipment applications may vary from specific component to component. Alloys such as 6061-T6 and 7075-T651 are commonly used in machine parts, tools, and industrial equipment.
6082 T651 Aluminum vs 6082 T6 Aluminum Plate
The main difference between 6082-T651 and 6082-T6 aluminum plate/sheet is their tempering process and resulting mechanical properties. Here's a comparison between the two:
Temper Condition
- 6082-T651: The "T651" temper designation indicates that the material has been solution heat treated, quenched, and then artificially aged. This process results in stable and stress-relieving conditions with maximum mechanical properties.
- 6082-T6: The "T6" temper designation indicates that the material has been solution heat treated and then artificially aged. This is a common tempering condition for aluminum alloys and provides good strength and toughness.
Mechanical Properties
- 6082-T651: This temper has higher mechanical strength compared to 6082-T6. It generally has a higher tensile and yield strength, making it suitable for applications requiring higher strength and load-bearing capacity.
- 6082-T6: While 6082-T6 has good strength, it may have slightly lower mechanical properties compared to 6082-T651. However, it still provides satisfactory strength for many applications.
Applications
- 6082-T651: This temper is typically used in applications requiring high strength and structural integrity. It is used in structural components, frames, and heavy-duty applications in industries such as aerospace, automotive, marine, and construction.
- 6082-T6: This condition is used in a wide variety of industries and applications including general engineering, construction, transportation, and sports equipment. It is suitable for applications requiring a balance of strength, formability, and processability.
Machinability
Both 6082-T651 and 6082-T6 aluminum plates/sheets have good machinability. However, the T6 temper may be easier to process due to its lower strength compared to T651.
The specific requirements of your application must be considered and the supplier or manufacturer must be consulted to determine the most suitable temper and material based on factors such as required strength, processability, and usability.